The Use of a Vickers Indenter in Depth Sensing Indentation
for Measuring Elastic Modulus and Vickers Hardness
© 2004
483
The Use of a Vickers Indenter in Depth Sensing Indentation
for Measuring Elastic Modulus and Vickers Hardness
Adonias Ribeiro Franco Jr.a, Giuseppe Pintaúdeb, Amilton Sinatoraa,
Carlos Eduardo Pinedoc, André Paulo Tschiptschina*
a
Dpto. de Eng. Metalúrgica e de Materiais and Dpto. de Eng. Mecânica, Escola Politécnica,
USP, Av. Prof. Mello Moraes, 2463, 05508-900 São Paulo - SP, Brazil
b
Dpto. Acadêmico de Mecânica, Centro Federal de Educação Tecnológica do Paraná
Av. Sete de Setembro, 3165, 80230-901 Curitiba - PR, Brazil
c
Núcleo de Pesquisas Tecnológicas, Universidade de Mogi das Cruzes
Av. Dr. Cândido Xavier de A. Souza 200, 08780-210 Mogi das Cruzes - SP, Brazil
Received: January 27, 2003; Revised: January 26, 2004
Depth sensing indentation is a powerful experimental technique for determining mechanical
properties of materials. In this work a computational routine was developed based on OliverPharr method for measuring a more precise values of elastic modulus using a Fischerscope
H100 - depth sensing indentation apparatus, with a Vickers indenter. This computational routine
aims also to measure Vickers hardness, as the equipment does not have software for this purpose.
From indentation data it was possible to determine initial unloading stiffness, contact depth, projected contact area, reduced modulus, elastic modulus and Vickers hardness of materials. The
validity of the routine was verified analyzing two coatings and nine bulk specimens with different
elastic-plastic behaviors.
It was verified that the elastic moduli determined through the software of the equipment resulted
in great discrepancies when low loads were applied. A good estimate of the elastic moduli of the
tested materials is given by the developed routine. For several testing loads, the diagonals determined by means of analytical procedure were compared with the same diagonals measured by image
analysis. A good estimate of the Vickers hardness of the above-mentioned materials is given by the
developed routine using different testing loads.
Keywords: depth sensing indentation, elastic modulus, Vickers hardness, Oliver-Pharr method,
ISE effect
1. Introduction
Load and displacement sensing indentation technique
allows determining mechanical properties at penetration
depths as low as 20 nm, avoiding the substrate effect on the
measurements1. The possibility to carry out tests in so small
scales makes this technique one of the tools chosen to characterize mechanical properties of thin films, coatings, second phase particles and magnetic hard disk recording media2-4.
A well defined indenter geometry is required to get well
defined indentation impressions. A perfect tip shape is difficult to achieve. Berkovich is a three-sided pyramid, and
*e-mail: aptschip@usp.br
Article presented at the XV CBECIMAT, Natal - RN, November/2002
provides a sharply pointed tip, compared to the Vickers
indenter, which is a four-sided pyramid and has a slight offset (0.5- µm)5,6. This is the main reason why three-sided
Berkovich indenters are used in depth sensing indentation
machines. However, any indenter with a sharp tip suffers
from a finite but an exceptionally difficult to measure tip
bluntness. Experimental procedures have been developed
to correct the tip shape, of both Vickers and Berkovich
indenters1, 7-10.
When tests are carried out with Berkovich indenters,
the registered data can be analyzed using the method pro-
484
Franco et al.
posed in 1992 by Oliver and Pharr7, which has its origins in
an earlier treatment by Doerner and Nix11. Nowadays, both
methods are accepted for the analysis of the indentation
data by the ISO/FDIS 14577-1 standard12. The Oliver-Pharr
method consists in a series of loading cycles to avoid thermal drift and plastic reversion, while the Doerner-Nix
method uses only a single cycle to obtain the indentation
data. The Fischerscope H100 - depth sensing indentation
machine uses the latter method, which is less time consuming and simpler but takes into account only a few data points,
leading to greater inaccuracy. Moreover, the Fischerscope
H100 uses the constant hardness calibration method8,13 to
correct the indenter tip shape, which is not adequate since
work-hardening may happen during the test.
The Oliver-Pharr method is widely used in depth sensing indentation machines with Berkovich indenter. However, it is equally applicable to the case depth sensing indentation using a Vickers indenter, with good results as mentioned in literature8,14,15. The depth sensing indentation
machine used in this work analyzes indentation data using
a software based on the Doerner-Nix method, and uses an
incorrect area function to describe the indenter tip shape,
leading to overestimated elastic modulus and hardness values due to ISE effect - indentation size effect16. Additionally, the Fischerscope apparatus software does not give
Vickers numbers, which are useful to compare with wellknown data of phases and micro-constituents given in literature.
The present work aims to develop a computational routine based on the Oliver-Pharr method for measuring more
precise values of elastic modulus and to obtain Vickers hardness numbers, using a Fischerscope H100 - depth sensing
indentation apparatus, equipped with a Vickers diamond
indenter.
2. Theoretical Aspects
Depth sensing indentation technique consists of printing an impression on the material surface by applying a
known load with an indenter of known geometry and subsequently analyzing the load vs. displacement data. Equations from the elastic punch theory can be used to determine the elastic modulus, E, and hardness, H, provided that
the following conditions during the initial withdrawal of
the indenter are ensured:
• the material’s recovery follows an elastic behavior;
• the contact area between the indenter and the specimen remains constant.
In this case, the Sneddon’s solutions17,18 for the case of
the indentation of an elastic half-space for a cylindrical
punch approach to the elastic behavior. One of the
Sneddon’s solutions leads to a simple relation between the
load, P, and the penetration depth, h, of the form:
Materials Research
(1)
where a is the radius of the cylinder; µ is the shear modulus;
and ν is Poisson’s ratio. Knowing that the area of the contact circle projected onto the surface, Ac, is equal to πa2 and
that the shear modulus is related to the elastic modulus in
the following way:
(2)
and substituting (2) in (1) and differentiating the obtained
expression with respect to h:
(3)
one can obtain the contact stiffness S = dP/dh. The elastic
modulus, E, can be taken directly from the initial unloading
slope, S, when Poisson’ ratio, ν, and contact area, Ac, are
given. The latter can be measured independently as a function of contact depth, hc.
As the elastic modulus of the indenter is not infinite,
Eq. 3 should be written in terms of combined elastic modulus specimen/indenter (Er), which is, according to Hertz
Equation:
(4)
where E, Ei, ν and ν i are the elastic moduli and Poisson’s
ratios of the specimen and indenter, respectively.
Therefore, for the indentation of a plane surface of a
semi-infinite elastic solid by a rigid punch, Eq. 3 can be
rewritten:
or
(5)
The above Equation shows that, for axisymmetric
indenters, the relationship between unloading stiffness, S,
and contact area, Ac, does not depend upon indenter geometry. Pharr, Oliver, and Brotzen19 have shown experimentally that the analysis used for determining elastic moduli
and contact areas from contact stiffness S is not limited to
punch geometry. Using finite elements method, King20 has
introduced to Eq. 5 a correction factor for non-axisymmetric
indenters:
(6)
Vol. 7, No. 3, 2004
The Use of a Vickers Indenter in Depth Sensing Indentation
for Measuring Elastic Modulus and Vickers Hardness
where b corresponds to a correction factor related to the lack of
symmetry of the indenter, which is equal to 1.0124 for Vickers
indenters, and Ac is the projected contact area.
Figures 1 to 3 show the main parameters used in
analyzing indentation data.
In Figs 1 and 2, hmax corresponds to the maximum depth,
a to the half-diagonal projected on the surface, hf to the
residual depth, hc to the contact depth, and hs to the deflection depth. In Fig. 3, S corresponds to the unloading stiffness for h = hmax.
As the unloading from hmax to hf is elastic, one of the
Sneddon’s solutions 8, for a conical punch (Figs. 1 and 2),
shows that the deflection of the surface at the contact is:
(7)
Another Sneddon’s solution shows that, for h = hmax, the
load is related to the elastic depth:
(8)
Substituting (7) in (8) and noting that the contact area
of interest is that at peak load, P = Pmax, it follows:
or
485
(10)
Therefore:
(11)
Considering that usually the indenters are not conical,
but square or triangular base pyramids (Vickers or Berkovich
indenters) it must take into account that for any revolution
paraboloyd (including Vickers indenters), ε is about 0.75 19.
As one can see in Fig. 4a, the contact area, Ac, can be
expressed as a function of the diagonal d 21:
(12)
Substituting this expression in Eq. 6, one obtains the
diagonal as a function of the indentation parameters:
(13)
Eventually, the Vickers hardness numbers can be determined by the average diagonal, d, estimated from such parameters:
(9)
(14)
To determine the contact depth from experimental data,
one can note that in Fig. 1:
Figure 1. Profile of the surface before and after indentation.
Figure 2. Main parameters used in analyzing unloading vs. indenter
depth curves.
Figure 3. Schematic representation of load-displacement data for
a depth sensing indentation experiment.
486
Franco et al.
Materials Research
Table 1 shows the main testing conditions.
In all cases the indentation depth did not surpass 10%
of the specimen thickness (film or substrate), avoiding any
contribution from the substrate22.
3.2. Materials
The materials used in this study were chosen in order to
include a wide range of hardness and elastic modulus values: PVD TiN and HVOF WC-12%Co coatings, alumina,
AISI D2 and AISI H13 tool steels, AISI 316 stainless steel,
aluminum, gold, soda-lime glass, Au-12%Pt and Co-25%Cr
odontological alloys. Table 2 presents elastic moduli for
these materials reported in the literature.
Bulk specimens were mechanically polished and finished
until 1 µm diamond paste. The AISI H13 tool steel specimens coated with TiN and with WC - 12%Co were carefully cleaned using an ultra-sound apparatus in alcohol bath
and subsequently dried in warm air. The WC-12%Co coating thickness is about 300 µm, while the TiN coating thickness is about 5 µm.
(a)
3.3. Analytical procedure used by Fischerscope equipment
(b)
Figure 4. a) Vickers indenter: Ac(d) = d2/2; β [≡ (180 - 2α)/2]= 22°;
and d = 2a. b) Under loading, the apex for Vickers indenter, 2Ψ, is
equal to 148°.
(15)
Fischerscope procedure for measuring hardness and elastic modulus consists in estimating the initial slope from
unloading data based on the Doerner-Nix analytical treatment and subsequently calculating the correct depth through
a calibration curve, previously established for tip-shape
indenter correction, frequently called hardness constant
method8,13.
Figure 5 shows the load-displacement data for alumina.
Considering the unloading curve, the initial unloading slope,
defined as contact stiffness, dP/dh = S, is determined taking the upper 1/3 of the unloading data and fitting it by a
linear relation of the form:
(16)
3. Experimental Details
where
3.1. Equipment and indentation procedure
A straight line is fitted to the unloading curve down to
its first 1/3 region and then extrapolated to zero, determining the depth hs and stiffness S.
Fitting the unloading data by a linear relation, yields
S = 0.4719 mN/nm and hs = 84 nm. Because the Vickers
indenter tip is not perfect, hmax is replaced by a corrected
depth, hcorr, in a depth function of the form:
A Fischerscope H100 - depth sensing indentation machine equipped with a Vickers diamond indenter, manufactured by Helmut Fischer GmbH, was used. Such equipment
allows applying loads from 1 mN to 1000 mN and registering penetration depths as a function of applied loads. Other
important testing characteristics of the equipment are:
• control of loading and unloading rates (dP/dt and
d √ P/dt);
• long or short delay times at maximum load;
• minimum step among indentations equal to 10 mm;
• definition of the number and position of the indentations (mapping).
.
(17)
where hcorr corresponds to equivalent depths from an ideal
Vickers indenter, and k and n are empirical parameters. The
surface area of the indenter is determined through the expression:
Vol. 7, No. 3, 2004
The Use of a Vickers Indenter in Depth Sensing Indentation
for Measuring Elastic Modulus and Vickers Hardness
(18)
In the above expression, the factor 26.43 is used instead
of 24.5 because the universal hardness Hu, taken for tip shape
calibration, is based on surface area of an ideal Vickers
indenter.
The surface area, A, together with the initial stiffness, S,
is then substituted in Eq. 6, yielding a value of 325.4 GPa
for reduced modulus, Er. Using Eq. 4 leads to E = 440 GPa
for alumina.
3.4. Oliver-Pharr Analytical Procedure
Referring to the unloading curve obtained experimentally for alumina (Fig. 5), one can note that it presents a
non-linear behavior. Pharr, Oliver, and Brotzen19 showed
that even metals present unloading curves with non-linear
behavior and that these curves are better described by nonlinear relationships.
In the Oliver-Pharr method7, the data taken from the
upper portion of the unloading curve (Fig. 5) are fitted by a
power-law relation of the form:
487
was verified that the contact stiffness, S, was underestimated.
Probably, this effect is associated with the limitation of the
Fischerscope equipment, which does not allow the inclusion of multiple cycles for minimizing the effects of thermal drift and plastic reversion.
Fitting the unloading data of Fig. 5 by a power law relation, it is obtained m equal to 1.386620 and A equal to
0.053065, as one can see in Fig. 6. Rearranging Eq. 19, the
residual depth can be predicted:
⇒
(20)
When P = Pmax = 50 mN, the maximum penetration depth,
h =hmax, is 270 nm. Substituting the values of m, A, P and h
in Eq. 20, a value of 130 nm is obtained for hf.
The contact stiffness, S, is obtained by means of Eq. 19
differentiating P with respect to h:
(21)
(19)
where P is the indenter load, m and A are empirical constants determined after unloading data fitting, hf is the residual depth, and h is the elastic displacement.
Although fittings corresponding to 80% of the unloading curve are recommended in the Oliver-Pharr method, the
fitting used in the present work was only 52%. When trying
to fit more than 52% of the data of the unloading curve, it
Table 1. Indentation conditions.
Number of measurements
Loading time, loading rate
Dwell time at maximum load (“creep”)
Unloading time, unloading rate
20
12 s, d√ P/dt
20 s
20s, d√ P/dt
Substituting the values of m, A and hf in Eq. 21, the
contact stiffness S = 0.4966 mN/nm is obtained.
The indenter-specimen contact depth, hc, can be obtained
using one of Sneddon’s solutions given in Eq. 11. Substituting the values of ε, Pmax and S in the referred expression,
a value of 195 nm is obtained for hc.
The projected contact area, Ac, can be determined through
the indenter area function, shown in Fig. 7.
This calibration curve for tip shape correction was previously established by means of an iterative procedure, called
the constant elastic modulus method, described by OliverPharr7. Fine fittings of the empirical constants were performed using an alternative method32 consisting of comparing the indentation diagonals measured by image analysis with that predicted through Eq. 13.
Table 2. Elastic moduli reported in literature for the used materials.
Material
Literature modulus (GPa)
WC-12%Co
495
TiN
417 (111)
Al2O3 (99.8%)
375, 393
Co-25%Cr
211
H13 tool steel
210
D2 tool steel
207
316 stainless steel
192, 195
Au-12%Pt
77
Au (99.98%)
77
Aluminum
70,4
Soda-lime glass
69,9
Reference
23
24
25, 26
27
28
28
29, 30
31
31
7
7
Figure 5. Load-displacement curve obtained experimentally for
an alumina (Al2O3) specimen.
488
Franco et al.
Then, substituting hc in the area function of the Vickers
indenter:
Ac = 2.197912 µm2
Then, after substituting this value together with that for
contact stiffness in Eq. 6, a value of 293.2 GPa for reduced
modulus Er is determined. Hence alumina modulus can be
determined by using the Hertz expression (Eq. 4):
E = 380.3 GPa
4. Discussion
4.1. Elastic Modulus
Materials Research
yielded by the software of the equipment, together with
values reported in the literature.
With respect to the values determined using the proposed
routine, a good agreement is observed when compared with
that reported in literature.
On the other hand, Table 3 shows that elastic moduli
measured by the equipment are overestimated for materials
with high elastic moduli. One can see in Table 3 that elastic
moduli determined for alumina, through the Fischerscope routine, are greater overestimated the less is the applied load.
This effect is known as indentation size effect - “ISE
effect”16, indicating that the analytical procedure used by
the equipment introduces inaccuracies when low loads are
applied. On the other hand, the proposed routine based on
Table 3 compares the results of elastic moduli measured
using the developed computational routine with that
Figure 6. Unloading curve fitted by a power law relation of the
form P = A (h - hf)m.
Figure 7. Area function, which takes into account roundness of
the Vickers indenter tip, determined previously by the constant elastic modulus method and image analysis.
Figure 8. Vickers impressions taken beneath the nitrided layer of
a H13 tool steel specimen. Load = 50 mN.
Figure 9. Vickers impression on top of aluminum. Load = 255 mN.
Vol. 7, No. 3, 2004
The Use of a Vickers Indenter in Depth Sensing Indentation
for Measuring Elastic Modulus and Vickers Hardness
489
Table 3. Comparison of elastic moduli measured by means of the analysis procedure based on Oliver Pharr method with those given by
Fischerscope machine. Each measurement corresponds to the average of twenty curves.
Material
Load, mN
WC-12%Co
50
100
30
50
500
1000
100
500
50
500
100
700
500
750
40
80
255
750
100
10
5
10
50
500
1000
TiN
Al2O3 (99.8%)
Co-25%Cr
H13 tool steel
D2 tool steel
AISI 316
stainless steel
Aluminum
Au-12%Pt
Au (99.98%)
Soda-lime glass
Experimental modulus
(new routine), GPa
477 ± 49
481 ± 42
411 ± 20
380 ± 18
378 ± 06
379 ± 05
209 ± 10
208 ± 10
208 ± 07
207 ± 07
206 ± 07
207 ± 05
196 ± 08
197 ± 06
70 ± 02
69 ± 02
70 ± 02
69 ± 03
81 ± 04
77 ± 06
68 ± 02
69 ± 01
70 ± 01
70
71
the Oliver and Pharr method gives elastic moduli practical
independent of the applied load, as one can see in Table 3.
4.2. Vickers Hardness
Figure 8 shows a set of measurements undertaken 5, 15,
25 and 35 µm beneath the nitrided surface of a H13 tool steel
specimen and Table 4 compares the diagonals measured by
image analysis with those determined by means of Eq. 13,
based on the calculated S and Er values. It can be seen that
the values given by both methods are very close.
Even in the case of large indentations (Fig. 9), the measured hardness values are in good agreement with those determined using Eq. 13, as can be seen in Table 5.
Finally, Table 6 shows the Vickers hardness numbers
determined through the proposed routine for different materials presenting different elastic-plastic behaviors and in
some cases obtained with different applied loads. The hardness values shown in Table 6 agree fairly well with the
well-known Vickers hardness numbers of the different listed
materials.
Therefore, artifacts in the measurements of the Vickers
Experimental modulus
(Fischer Software), GPa
526± 61
509± 40
510 ± 30
442 ± 19
410 ± 06
405 ± 05
230 ±10
210 ±10
220 ± 07
210 ± 05
230 ± 05
215 ± 07
182 ± 08
189 ± 6
69 ± 02
68 ± 02
68 ± 02
65 ± 03
80 ± 02
74 ± 02
79 ± 02
78 ± 01
80 ± 01
80
80
Literature
modulus, GPa
490
417 (111)
375, 393
211
210
207
192, 195
70.4
77
77
69.9
hardness owing to ISE effect alone can be ruled out. The
new routine adapted to Fischerscope - depth sensing indentation apparatus allows measuring Vickers hardness of
tribological coatings using very low loads without the necessity to derive expressions that relate coating hardness to
substrate hardness, and to deal with the composite response
of film and substrate.
5. Conclusion
• The proposed routine gives a better estimate of elastic moduli of materials, when compared to the values
given by the equipment software.
• The lesser the load, the greater are the differences
between the two methods.
• Very low loads can be used for determining elastic
moduli of very thin layers, as the ISE effect was minimized.
• The elastic contact theory equations and the OliverPharr approach offer an optimum prediction of the
indentation diagonals and, consequently, of the
Vickers hardness numbers of the tested materials.
490
Franco et al.
Materials Research
Table 4. Indentation diagonals beneath the surface in a nitrided specimen, determined by means of Eq. 13 and measured by image
analysis. Maximum load: 50 mN.
Distance from the nitrided surface
(µm)
~5
~15
~25
~35
Average diagonal using Eq. 13
(µm)
3.19 ± 0.07
3.80 ± 0.08
4.02 ± 0.06
4.04 ± 0.07
Table 5. Comparison of Vickers hardness number determined using Eq. 11 with that measured by image analysis for an aluminum
specimen. Load = 255 mN.
Average diagonal, d
Area, AVickers Vickers number, HV
(µm)
(µm2)
(kgf/mm2)
35.14 (Eq. 13)
665.96
38
34.65 (Image analysis) 647.46
39
Table 6. Hardness Vickers determined experimentally using different loading, for materials of different elastic-plastic behaviors.
Material
Hardness Vickers,
kgf/mm2
5.0 µm TiN coating
2421 ± 119
Al2O3 (99.8%)
2005 ± 50
1947 ± 81
2028 ± 135
300 µm WC-12%Co coating 1399 ± 167
1455 ± 90
AISI D2 tool steel
650 ± 59
Soda-lime glass
550 ± 0 2
AISI H13 tool steel
485 ± 17
481 ± 9
Co-25%Cr
398 ± 35
403 ± 35
316 stainless steel
228 ± 7
Au (99.98%)
217 ± 11
Au-12%Pt
194 ± 14
Aluminum
35 ± 4
Load,
mN
30
1000
500
50
50
100
250
50
50
500
100
500
750
10
100
750
Acknowledgments
The financial support of the FAPESP, Fundação de
Amparo à Pesquisa do Estado de São Paulo, is gratefully
acknowledged.
References
1. Pethica, J.B.; Hutchings, R.; Oliver, W.C. Hardness measurement at penetration depths as small as 20 nm. Philo-
Average diagonal, using Image analysis
(µm)
3.20 ± 0.1
3.81 ± 0.1
4.00 ± 0.2
4.03 ± 0.2
sophical Magazine A, v. 48, n. 4, p. 593-606, 1983.
2. Pharr, G.M. Measurement of mechanical properties by
ultra-low load. Materials Science and Engineering A,
v. 253, n. 1-2, p. 151-159, 1998.
3. Carvalho, S.; Vaz F.; Rebouta, L.; Schneider, D.;
Cavaleiro, A.; Alves, E. Elastic properties of (Ti,Al,Si)N
nanocomposite films. Surface and Coatings Technology, v. 142-144, p. 110-116, 2001.
4. Lo, R.Y; Bogy, D.B. Compensating for elastic deformation of the indenter in hardness tests of very hard materials. Journal of Materials Research, v. 14, n. 6, p. 227622, 1998.
5. Bhushan, B.; Gupta, B.K. Macro and Micro mechanical
and tribological properties. In: Handbbok of Hard Coatings - Deposition Technologies, Properties and Applications. Bunshah, R.F. Ed. - Noyes Publications, Park
Ridge, New Jersey, USA, p. 550, 2001.
6. Trindade, A.C.; Cavaleiro, A.; Fernandes, J.V. Estimation of Young’s modulus and of hardness by ultra-low
load hardness tests with a Vickers indenter. Journal of
Testing and Evaluation, v. 22, n. 4, p. 365-369, 1994.
7. Oliver, W.C.; Pharr, G.M. A new improved technique
for determining hardness and elastic modulus using load
and sensing indentation experiments. Journal of Materials Research, v. 7, n. 6, p. 1564-1582, 1992.
8. Seitzman, L.E. Mechanical properties from instrumented
indentation: uncertainties due to tip-shape correction.
Journal of Materials Research, v. 13, n. 10, p. 29362944, 1998.
9. Herrmann, K.; Jennett, N.M.; Wegener, W., Meneve, J.,
Hasche, K.; Seemann, R. Progress in determination of
the area function of indenters used for nanoindentation.
Thin Solids Films, v. 377-378, p. 394-400, 2000.
10. Thurn, J.; Cook, F. Simplified function for sharp
indenter tips in depth-sensing indentation. Journal of
Materials Research, v. 17, n. 5, p. 1143-1146, 2002.
11. Doerner, M.F.; Nix, W.D. A method for interpreting the
data depth-sensing indentation instruments. Journal
of Materials Research, v. 1, n. 4, p. 601-609, 1986.
12. ISO/FDIS 14577-1. Metallic materials - Instrumented
indentation test for hardness and material parameter,
Part 1: Test method. ISO - International Organization
Vol. 7, No. 3, 2004
The Use of a Vickers Indenter in Depth Sensing Indentation
for Measuring Elastic Modulus and Vickers Hardness
for Standardization, Geneve, Switzerland, 2002.
13. Weiler, W.W. Dynamic loading - a new microhardness
test method. Journal of Testing and Evaluation, v. 18,
n. 4, p. 229-239, 1990.
14. Atar, E.; Cimenoglu, H.; Kayali E.S. Hardness characterisation of thin Zr (Hf,N) coatings. Surface and Coatings Technology, v. 162, n. 2-3, p. 167-173, 2003.
15. Strange D.J; Varshneya, A.K. Finite element simulation of microindentation on aluminum. Journal of Materials Science, v. 36, p. 1943-1949.
16. Iost, A.; Bigot, R. Indentation size effect: Reality or
artefact?. Journal of Materials Science, v. 31, n. 13,
p. 3573-3577, 1996.
17. Harding, J.W.; Sneddon, I.N. The elastic stresses produced by the indentation of the plane surface of a semiinfinite elastic solid by a rigid punch. In: Proc. Cambridge Philos. Soc., v. 41, p. 16-26, 1945.
18. Sneddon, I.N. The relation between load and penetration in the axisymmetric Boussinesq’ problem for a
punch of arbitrary profile. International Journal of Science Engineering, v. 3, p. 47-57, 1965.
19. Pharr, G.M.; Oliver, W.C.; Brotzen, F.R. On the generality of the relationship among contact stiffness, contact area, and elastic modulus during indentation. Journal of Materials Research, v. 7, n. 3, p. 613-617, 1992.
20. King, R.B. Elastic analysis of some punch problems
for a layered medium. International Journal of Solids
Structures, v. 23, n. 12, p. 1657-1664, 1987.
21. Loubet, J.L.; Georges, J.M.; Marchesini, O.; Meillee,
G. Vickers indentation curves of magnesium oxide
(MgO). Journal of Tribology, v. 106, p. 43-48, 1984.
22. Johnson, K.L. The correlation of indentation experiments. Journal of Mechanics and Physics of Solids,
v. 18, p. 115-126, 1970.
23. Chawla, N.; Patel, B.V.; Koopman, M.; Chawla K.K.,
Saha R., Patterson B.R., Fuller E.R., Langer S.A. Micro
24.
25.
26.
27.
28.
29.
30.
31.
32.
491
structure-based simulation of thermomechanical
behavior of composite materials by object-oriented finite element analysis. Materials Characterization,
v. 49, n. 5, p. 395-407, 2002.
Zhang, M.; He, J. Ab-initio calculation of elastic constants of TiN. Surface and Coatings Technology, v.142,
p.125-131, 2001.
Zeng, K.; Söderlund, E.; Giannakopoulos, E.A.; Rowcliffe,
D.J. Controlled indentation: a general approach to determine mechanical properties of brittle materials. Acta
Materialia, v. 44, n. 1, p. 1127-1141, 1996.
Giannakopoulos, E.A.; Larsson, P-L. Analysis of pyramid indentation of pressure-sensitive hard metals and
ceramics. Mechanics of Materials, v. 25, p. 1-35, 1997.
Morris, H.F. Properties of cobalt-chromium metal ceramic alloys after heat treatment. J. Prosthet. Dent.,
v. 62, p. 426-433, 1989.
Antunes, J.M.; Cavaleiro, A.; Menezes, L.F.; Simões,
M.I.; Fernandes J.V. Ultra-microhardness testing procedure with Vickers indenter. Surface and Coatings
Technology, v. 149, n. 1, p. 27-35, 2002.
Tran, M.D.; Poublan J.; Dautzenberg, J.H. A practical
method for the determination of the Young’s modulus
and residual stresses of PVD thin films. Thin Solids
Films, v. 308-309, p. 310-314, 1997.
Leyland, A.; Matthews, A. On the significance of the
H/E ratio in wear control: a nanocomposite coating approach to optimised tribological behaviour. Wear, v. 246,
p. 1-11, 2000.
Craig, R.G.; Peyton, F.A.; Johnson, D.W. Compressive
properties of enamel, dental cements and gold. J. Dent.
Res., v. 40, n. 5, p.936-945, l961.
Franco Jr., A.R. Obtenção de revestimentos dúplex por
nitretação a plasma e PVD-TiN em aços ferramenta
AISI H13 e AISI D2. Tese de doutorado, p. 178, EPUSP,
São Paulo, SP, 2003.